LD393TG/M is a calendered PVC vinyl with repositionable adhesive & LG Hausys's AiRFREE ™ technology. It's designed for solvent-based inkjet printing and guarantees up to 5-years outdoor durability. AiRFREE ™ technology allows trapped air to be released during application. AiRFREE ™ is LG Hausys's proprietary technology that utilizes embossing patterns on the release liner, making it easier to remove trapped bubbles and increasing overall efficiency and productivity.
Areas of use
- Solvent inkjet printing: Vutek, Arizona, Mimaki, Mutoh, Roland, DGI etc.
- Outdoor display, sign, exhibition stand, automotive advertising
⇒ The films conform well to flat and seamed surfaces, when processed and applied according to LG Hausys's recommendations.
- 5years durable calendered film
- Excellent printing performance
- Dimensional stability and performance under a wide range of physical and climatic conditions
- Excellent weather resistance: Solvent based acrylic adhesive (Repositionable Type)
- Liner : Super flat, double side PE coated paper
- Standard Width: 30”, 54”, 60”
- Standard Length: 50yd
|Film||3.2mils(80㎛) opaque film with gloss finish|
|Thickness||4.3mils(110㎛) with adhesive (± 10%)|
|Adhesive||Acrylic based pressure sensitive(Solvent based)|
|Liner||Double side PE coated paper|
|Application surfaces||Flat, slightly curved surfaces|
|Application temp.||≥10℃(18 to 25℃ optimum)|
Durability is based on field experience and exposure tests in South Korea. Outdoor durability is 5 years when properly processed and applied (unprinted film vertical exposure).
Shelf life is 1 year from factory shipment.
Storage condition: Free from excessive moisture, temperature, direct sunlight (20℃ x 50% R.H)
|Property||Metric Units||Test Method|
|Thickness (Including adhesive)||4.3mils(110㎛) ± 10%||Micrometer|
|Tensile strength||≥ 1.8kg/cm²||ASTM D882|
|Elongation||≥ 100%||ASTM D882|
|Peel adhesion(24hrs)||≥ 1,400g/in||180 peeling PSTC-1|
|Service temp. range||-25℃ ~ 82℃||Film applied Al panels 24hrs prior test|
|Application temp.||≥ 10℃||18 to 25℃ optimum, on clean substrate|
|Opacity||Tt ≤ 10||Haze Meter (Tt: Transmission)|
|Gloss||60 ↑||@60, in Machine Direction|
|Dimensional Stability||Max 0.5mm||Adhered to Aluminum Plate, Length Direction
(80℃ Oven, 24hr , Average)
|Release liner thickness||0.14mm|